Research advances in residual thermal stress of ceramic/metal brazes

Brazing, as a common method of bonding ceramic and metal, has been applied in microelectronics, aerospace, machinery and other domains extensively. The residual thermal stress in the brazed joint has direct effects on the mechanical properties of the joint, so how to control the generation of residual thermal stress has become the vital point. In this paper, the methods of reducing residual thermal stress in the brazing process in recent years are reviewed. The generation and effects of residual thermal stress in the brazed joint are introduced. Besides, the methods of detecting residual thermal stress are discussed, and different methods of reducing residual thermal stress in brazed joints are also analyzed. Finally, the future development directions of reducing residual thermal stress in the brazed joint are proposed.     

Thermal and dynamic mechanical behavior of epoxy composites reinforced with post-consumed yerba mate

Yerba mate (YM) is widely consumed in Latin American countries, and its residues can be used as bio-resources such as reinforced in epoxy composites. The present work aims to produce epoxy resin composites and evaluate the influence of post-consumed YM as reinforcement. The concentrations of YM used were 5, 10, and 20% (wt/wt). Chemical, thermal, morphological, and dynamic mechanical behaviors were explored. The YM incorporation did not influence chemically on the epoxy structure and a pull-out phenomenon was observed as YM content increased. The YM at lower concentrations (5 and 10%) led to higher values of activation energies calculated from model-free isoconversional methods. On the other hand, the composite e/YM 20 wt% improved all dynamic-mechanical properties. YM proved to be a suitable and cheap reinforcement for epoxy resin.     

Wear and thermal behavior of basalt fiber reinforced rice husk/polyvinyl chloride composites

Plant fiber reinforced polymer composites (PFRPs) in practical application are often subjected to both complex friction and variable temperature environments. The present work explores the possibility of reinforcing rice husk/polyvinyl chloride (RH/PVC) composites with basalt fibers (BF) for developing a new wear resistant material with improved thermal stability. The results showed that the structural strength and wear resistance of the composites increased at first and then decreased with an increasing ratio of BF/RH, the highest value occurred at a BF/RH ratio of 8/42. The thermal stability of composites had a positive relationship with BF/RH ratio. The composites added with BF all possessed improved performance in comparison with unadded composites. Hence, the findings of this article proposed some new perspectives on improving the wear resistance and thermal stability of PFRPs that would broaden their practical application.     

采用温控和碘吸收池技术的发射激光稳频技术

多普勒测风激光雷达通过分析系统回波信号的多普勒频移反演出风速，为提高风场探测精度，从稳频技术方面展开研究。在稳频过程中，分别采取措施消除激光频率的长期漂移和短期抖动。针对激光频率的长期漂移，设计并研制了种子激光器温控箱，通过水浴的控温方式大大减小了激光频率的长期漂移，将激光频率稳定在±50 MHz以内；针对激光频率的短期抖动，采用以碘分子吸收池为核心器件的稳频系统，通过半导体控温方式对碘分子吸收池精确控温，控温精度达0.03 ℃，提高了稳频精度，将激光频率进一步稳定在±8 MHz以内，满足±10 MHz以内的设计精度要求。通过搭建多普勒测风激光雷达系统，对发射激光稳频装置进行系统验证，连续4组风场观测结果表明:系统探测高度为17 km，绝大部分方差在4 m/s以下，满足测风激光雷达测量指标的要求。     

Effect of atmosphere control on magnetic properties of CaO-Al2O3-SiO2-Fe3O4 glass ceramics

The influences of atmosphere during processes of melting and heat treatment, heat treatment temperature, Fe₃O₄ content and basicity on the magnetic properties of magnetite-based glass ceramics were investigated. For sample containing 20 % Fe₃O₄ melted in different atmospheres, the highest saturation magnetisation was realized in 20vol% air + 80 vol% Ar, due to the fact that ratio of Fe³⁺ to Fe²⁺ in melt obtained in this atmosphere was close to 2. However, it was found that the coercivity of glass ceramics was not affected by the melting atmosphere. A high sintering temperature led to the decrease of saturation magnetisation and the increase of coercivity. As increasing Fe₃O₄ content, the main crystal phase transformed from CaSiO₃ to CaFe_0.6Al_1.3Si_1.08O₆ and finally to magnetite phase, accompanied by the increase of saturation magnetisation and coercivity. In addition, the increase of basicity caused the decrease of saturation magnetisation and the increase of coercivity.